TRBF90 (PBAT Modified Resin For Film)
Component: PBAT,starch,PLA
Appearance: Light yellow resin
Density: 1.15-1.18g/cm3 (ISO1183)
Melting Point: 110-120℃ (DSC, 10℃/min)
Melt Flow index: ≤10g/10min,(190℃, 2.16kg) (ISO 1133)
Tensile Strength: ≥16 MPA (ISO 527)
Elongation at Break: ≥180% (ISO527)
Bending Strength: ≥4MPA (ISO178)
Flexural Modulus: ≥100MPA (ISO178)
Features:
1.100% compostable.
2.Compared to the traditional plastic ,save over 30% petrochemical resource,
3.compared to the traditional plastic, reducing over 40% co2 emissions.
4.No phthalate, no bisphenol A, non-toxic and pollution-free.
5.Have mechanical properties, could be applied to general plastic
processing facilities for various modding processing.
Component: PBAT,starch,PLA
Appearance: Light yellow resin
Density: 1.15-1.18g/cm3 (ISO1183)
Melting Point: 110-120℃ (DSC, 10℃/min)
Melt Flow index: ≤10g/10min,(190℃, 2.16kg) (ISO 1133)
Tensile Strength: ≥16 MPA (ISO 527)
Elongation at Break: ≥180% (ISO527)
Bending Strength: ≥4MPA (ISO178)
Flexural Modulus: ≥100MPA (ISO178)
Features:
1.100% compostable.
2.Compared to the traditional plastic ,save over 30% petrochemical resource,
3.compared to the traditional plastic, reducing over 40% co2 emissions.
4.No phthalate, no bisphenol A, non-toxic and pollution-free.
5.Have mechanical properties, could be applied to general plastic
processing facilities for various modding processing.
Main Products
biodegradable & compostable bags, biodegradable & compostable material