TRBF95(PLA Modified Resin For Film)
Component:PLA,PBAT
Appearance: Nature white resin
Density: 1.2-1.3g/cm3 (ISO1183)
Melting Point: 155-170℃ （DSC, 10℃/min）
Melt Flow index: ≤15g/10min,(190℃, 2.16kg) (ISO 1133)
Tensile Strength: ≥20 MPA (ISO 527)
Elongation at Break: ≥150% （ISO527）
Bending Strength: ≥15MPA (ISO178)
Flexural Modulus: ≥500MPA (ISO178)
Features:
1.100% compostable.
2.Compared to the traditional plastic, saving over 75% petrochemical resource,
3.Compared to the traditional plastic reducing over 60% co2 emission.
4.No phthalate, no bisphenol A, non-toxic and pollution-free.
5.Have mechanical properties, could be applied to general plastic processing facilities for various modding processing.
6.Transparency and softness could be customized as required
Component:PLA,PBAT
Appearance: Nature white resin
Density: 1.2-1.3g/cm3 (ISO1183)
Melting Point: 155-170℃ （DSC, 10℃/min）
Melt Flow index: ≤15g/10min,(190℃, 2.16kg) (ISO 1133)
Tensile Strength: ≥20 MPA (ISO 527)
Elongation at Break: ≥150% （ISO527）
Bending Strength: ≥15MPA (ISO178)
Flexural Modulus: ≥500MPA (ISO178)
Features:
1.100% compostable.
2.Compared to the traditional plastic, saving over 75% petrochemical resource,
3.Compared to the traditional plastic reducing over 60% co2 emission.
4.No phthalate, no bisphenol A, non-toxic and pollution-free.
5.Have mechanical properties, could be applied to general plastic processing facilities for various modding processing.
6.Transparency and softness could be customized as required
Main Products
biodegradable & compostable bags, biodegradable & compostable material