sj301
SJ301
It is silicon calcium netural sinter flux with basicity of 1.0, black in color and round grain shape,loose density 2.0-0.28mm(10-60mesh)
It has advantages of stable arc combustion, good slag detachablity and good appearance of weld.
Application:
Working with welding wire(H08A、H08MnA、H08MnMoA), it can weld common steel sturcure, boiler steel and pipeline steel.
Conform with:AWS A5.17: F6A0-EL8,F7A0-EM12
Cautions: 1.The oil soil,moisture,iron rust and other foreign substances must be removed from the welding joint. 2.The welding flux must be baked under 300-350°C for 2 hours when affected with damp. 3.Its better to use direct current.
(Chemical Composition)
SiO2+TiO2 Al2O3+MnO CaO+MgO CaF2 S P
30~40 25~30 20~30 5~13 ≤0.05 ≤0.05
(Mechanical Performance of the Deposited Metal):
Wires Standard Models 6s (Mpa) 6b (Mpa) δ5 Akv (J)
HO8A HO8MnA F4A2-HO8A F5A4-HO8MnA ≥350 ≥410 ≥420 ≥500 ≥22% ≥22% ≥27(-20°C)
maito: shizhenggggg@hzliulian.com
It is silicon calcium netural sinter flux with basicity of 1.0, black in color and round grain shape,loose density 2.0-0.28mm(10-60mesh)
It has advantages of stable arc combustion, good slag detachablity and good appearance of weld.
Application:
Working with welding wire(H08A、H08MnA、H08MnMoA), it can weld common steel sturcure, boiler steel and pipeline steel.
Conform with:AWS A5.17: F6A0-EL8,F7A0-EM12
Cautions: 1.The oil soil,moisture,iron rust and other foreign substances must be removed from the welding joint. 2.The welding flux must be baked under 300-350°C for 2 hours when affected with damp. 3.Its better to use direct current.
(Chemical Composition)
SiO2+TiO2 Al2O3+MnO CaO+MgO CaF2 S P
30~40 25~30 20~30 5~13 ≤0.05 ≤0.05
(Mechanical Performance of the Deposited Metal):
Wires Standard Models 6s (Mpa) 6b (Mpa) δ5 Akv (J)
HO8A HO8MnA F4A2-HO8A F5A4-HO8MnA ≥350 ≥410 ≥420 ≥500 ≥22% ≥22% ≥27(-20°C)
maito: shizhenggggg@hzliulian.com