Product Description
Welding flux SJ101 Fluoric alkali sintering solder, with basicity of 1.6-1.8, loose density 1.2-1.25 g/cm3 and grain size 10-60 mesh.
It has excellent performance of anti-hygroscopic, large grain size, low loose density and low consumption.
Application:
Working with H08MnA、H08MnMo、H10Mn2、H08C;
Used in different kinds of low alloy steel structure.
Conform with:AWS A5. 17 EH-14
Typical weld metal analysis: (Wt%)
C : 0.05 , Si: 0.23 , Mn : 1.80 , S: 0.022 , P: 0.028
Typical Flux Composition Range:
SiO2+TiO2:20-30%, CaO+MgO:25-35%, Al2O3+MnO:20-30%, CaF2:15-25%,8.
Typical weld metal mechanical properties:
Yield stress: ≥400Mpa , Tensible strength :480-660Mpa , Elongation: ≥22% ,
AKV(J)27/ -40deg
Packing: Plastic-lined paper bag of 25KG each. 1000kg/pallet10.
Storage:To ensure the integrity of welding flux over an extended period, flux should be stored indoors in a dry place. Moist flux can be redried at300-350°C for 2 hours. Both heating and cooling must be carried out slowly.
mailto: shizhenggggg@hzliulian.com
Welding flux SJ101 Fluoric alkali sintering solder, with basicity of 1.6-1.8, loose density 1.2-1.25 g/cm3 and grain size 10-60 mesh.
It has excellent performance of anti-hygroscopic, large grain size, low loose density and low consumption.
Application:
Working with H08MnA、H08MnMo、H10Mn2、H08C;
Used in different kinds of low alloy steel structure.
Conform with:AWS A5. 17 EH-14
Typical weld metal analysis: (Wt%)
C : 0.05 , Si: 0.23 , Mn : 1.80 , S: 0.022 , P: 0.028
Typical Flux Composition Range:
SiO2+TiO2:20-30%, CaO+MgO:25-35%, Al2O3+MnO:20-30%, CaF2:15-25%,8.
Typical weld metal mechanical properties:
Yield stress: ≥400Mpa , Tensible strength :480-660Mpa , Elongation: ≥22% ,
AKV(J)27/ -40deg
Packing: Plastic-lined paper bag of 25KG each. 1000kg/pallet10.
Storage:To ensure the integrity of welding flux over an extended period, flux should be stored indoors in a dry place. Moist flux can be redried at300-350°C for 2 hours. Both heating and cooling must be carried out slowly.