Property Unit Test Method Test Condition
Tensile Strength kg/cm2
( MPa) ASTM
D-638
( ISO527) 23℃ 220
(22)
Tensile Elongation % ASTM
D-638
( ISO527) 23℃ 40
Flexural Strength kg/cm2
( MPa) ASTM
D-790
( ISO178) 23℃ 440
(43)
Flexural Modulus kg/cm2*104
( MPa) ASTM
D-790
( ISO178) 23℃ 2.3
(2260)
Izod
Impact Strength kg-cm/cm
( J/m ) ASTM
D-256
( ISO R180 ) 23℃
1/4\ bar 11.0
(108)
Vicat Softening
Temperature ℃ ASTM
D-1525
(ISO306B) Annealed
80℃×2Hr
1/8\ bar 95
Heat Deflection
Temperature ℃ ASTM
D-648
( 75/A) Annealed
80℃×2Hr
1/8\ bar 88
Melt
Flow Index g/10 min ASTM
D-1238
( ISO1133 ) 200℃×5Kg
( 49N ) 5.5
Residual Monomer ppm max. 700
Molding
Shrinkage % FCFC
Method 23℃ 0.4~0.6
Specific Gravity ASTM
D-792
( ISO1183 ) 23℃/23℃ 1.04
Flammability UL-94 FILE NO.
E162823 1/16" HB
NC
Tensile Strength kg/cm2
( MPa) ASTM
D-638
( ISO527) 23℃ 220
(22)
Tensile Elongation % ASTM
D-638
( ISO527) 23℃ 40
Flexural Strength kg/cm2
( MPa) ASTM
D-790
( ISO178) 23℃ 440
(43)
Flexural Modulus kg/cm2*104
( MPa) ASTM
D-790
( ISO178) 23℃ 2.3
(2260)
Izod
Impact Strength kg-cm/cm
( J/m ) ASTM
D-256
( ISO R180 ) 23℃
1/4\ bar 11.0
(108)
Vicat Softening
Temperature ℃ ASTM
D-1525
(ISO306B) Annealed
80℃×2Hr
1/8\ bar 95
Heat Deflection
Temperature ℃ ASTM
D-648
( 75/A) Annealed
80℃×2Hr
1/8\ bar 88
Melt
Flow Index g/10 min ASTM
D-1238
( ISO1133 ) 200℃×5Kg
( 49N ) 5.5
Residual Monomer ppm max. 700
Molding
Shrinkage % FCFC
Method 23℃ 0.4~0.6
Specific Gravity ASTM
D-792
( ISO1183 ) 23℃/23℃ 1.04
Flammability UL-94 FILE NO.
E162823 1/16" HB