Material
Central electrode: ferrite-chrome wire; stainless steel; etc.
Insulator: alumina-ceramics
2). Characteristics
No discharge or abnormal current when 10 kV AC voltage is applied for minute or more.
Insulation resistance between electrode wire and ground is to be 100 MΩ or higher when measured by 500 V megger.
No electrode cracking and no abnormality of electrode fixed strength, etc. after electrode tip is heated for 1 hour at 600℃.
No abnormality caused by rapid cooling after heating for 10 minutes at a water temperature of +120℃.
Material
Central electrode: ferrite-chrome wire; stainless steel; etc.
Insulator: alumina-ceramics
2). Characteristics
No discharge or abnormal current when 10 kV AC voltage is applied for minute or more.
Insulation resistance between electrode wire and ground is to be 100 MΩ or higher when measured by 500 V megger.
No electrode cracking and no abnormality of electrode fixed strength, etc. after electrode tip is heated for 1 hour at 600℃.
No abnormality caused by rapid cooling after heating for 10 minutes at a water temperature of +120℃.
Material
Central electrode: ferrite-chrome wire; stainless steel; etc.
Insulator: alumina-ceramics
2). Characteristics
No discharge or abnormal current when 10 kV AC voltage is applied for minute or more.
Insulation resistance between electrode wire and ground is to be 100 MΩ or higher when measured by 500 V megger.
No electrode cracking and no abnormality of electrode fixed strength, etc. after electrode tip is heated for 1 hour at 600℃.
No abnormality caused by rapid cooling after heating for 10 minutes at a water temperature of +120℃.
3) Application: Mainly used in BBQ Gas Grill, gas water heater, furnace, etc
Central electrode: ferrite-chrome wire; stainless steel; etc.
Insulator: alumina-ceramics
2). Characteristics
No discharge or abnormal current when 10 kV AC voltage is applied for minute or more.
Insulation resistance between electrode wire and ground is to be 100 MΩ or higher when measured by 500 V megger.
No electrode cracking and no abnormality of electrode fixed strength, etc. after electrode tip is heated for 1 hour at 600℃.
No abnormality caused by rapid cooling after heating for 10 minutes at a water temperature of +120℃.
Material
Central electrode: ferrite-chrome wire; stainless steel; etc.
Insulator: alumina-ceramics
2). Characteristics
No discharge or abnormal current when 10 kV AC voltage is applied for minute or more.
Insulation resistance between electrode wire and ground is to be 100 MΩ or higher when measured by 500 V megger.
No electrode cracking and no abnormality of electrode fixed strength, etc. after electrode tip is heated for 1 hour at 600℃.
No abnormality caused by rapid cooling after heating for 10 minutes at a water temperature of +120℃.
Material
Central electrode: ferrite-chrome wire; stainless steel; etc.
Insulator: alumina-ceramics
2). Characteristics
No discharge or abnormal current when 10 kV AC voltage is applied for minute or more.
Insulation resistance between electrode wire and ground is to be 100 MΩ or higher when measured by 500 V megger.
No electrode cracking and no abnormality of electrode fixed strength, etc. after electrode tip is heated for 1 hour at 600℃.
No abnormality caused by rapid cooling after heating for 10 minutes at a water temperature of +120℃.
3) Application: Mainly used in BBQ Gas Grill, gas water heater, furnace, etc
Features
.BBQ ElectrodesMain Products
BBQ Spark Electrodes