Features

• Technical characteristics
• Drying time: 15 minutes
• Open time: 24 hours (approx.)
• Viscosity: 14 minutes (ZAHN CUP method)
• Stability: 12 months
• Base: synthetic rubber (neoprene)
• Color: translucent dark yellow
• Green strength: excellent
• Heat resistance: good
• Applications
• Shoe & textile industry: Natural leather sole adherence to leather and textiles. Semi expanded sole adherence to leather and textiles. Leather adherence to leather textile folding. Permanent bonding of soles to shoes, sole laying, lasting etc. Excellent for shoe repair at home. No nails , no press, no stitching.
• Furniture industry: Adhering formica table tops, wood or plastic veneers and component parts of furniture.
• Automotive industry: Bonding of weather stripping and gaskets. Under coating, patching convertible tops etc.
• Building industry: Bonding of plastic and rubber tiles to floors, walls, partitions etc. Bonding of leather stripping to windows and doors. Adhering honey-comb panel assemblies etc.
• Miscellaneous: Seaming and patching of tarpaulins, tents, rainwear and various inflatable structures. Adhering fabric to metal and other nonporous material and many more uses.
• Directions for use
• Clean, dry and roughen both surfaces thoroughly.
• Apply thin even coating over both surfaces. On porous surfaces like leather and textiles two coats are preferable.
• Allow the films to dry for 15 to 30 minutes(depending upon the substrates) until they are completely dry.
• Join the surfaces taking care not to trap any air and press, hammer or roll down firmly. Prolonged pressure not necessary.
• If the film dries before bonding, it can be reactivated with heat or solvent even after several days, to give a satisfactory bond strength.
• The bond grows stronger with age and should be tested after 48 hours.
• The adhesive is flammable. Do not use or keep near fire or flame.
• Presentation
• In cans, tins and tubes of various quantities. Special packing requirements can be met on request.
• Heat resistance
• Two 1"x 8" long leather strips bonded with Samad Bond Super when subjected to temperature of 80 Celsius would easily with stand a peeling load of 2kgs applied at the strips at angle of 90 Celsius.